Effect of Stirring Speed on Characteristics of Fe3O4 Nanoparticles Coated with Polyvinyl Alcohol and Glutaldehyde as a Crosslinker

Lale Budi Hutami Rahayu, Ika Oktavia Wulandari, Djoko Harry Santjojo, Akhmad Sabarudin

Abstract


Research on Fe3O4 nanoparticles is mostly done because of the unique nature of Fe3O4 which has magnetic properties, non-toxic, biocompatible and easily degraded so it is interesting to investigate as a drug delivery system. This nanoparticles were successfully synthesized by coprecipitation method with variations of stirring rate were 180 rpm (sample A), 250 rpm (sample B) and 320 rpm (sample C). FTIR analysis of Fe3O4 nanoparticles, was absorption at ~585 cm-1 for samples A and B showing the presence of Fe-O magnetite bond and absorption at ~623 cm-1 which were not very sharp for maghemite. However the sample B, only absorption at ~623 cm-1 which is sharp for maghemite (γ-Fe2O3) because of Fe2O3 cubic is not formed. SEM analysis did not show significant morphological differences in velocity variation. From XRD analysis known that the crystal size for samples A and B respectively of 6.4192 nm and 9.5513 nm for sample C could not be calculated because of many iron oxide phases present in it, so it is difficult to find FWHM. ESR analysis of nanoparticle samples shown Fe3O4 properties were ferromagnetic.


Keywords


Nanoparticles, Magnetite (Fe3O4), Copresipitation, Polyvinyl Alcohol, Glutaraldehyde

Full Text:

PDF

References


Santos, M.C., Seabra, A.B., Pelegrino, M.T. and Haddad, P.S. (2016) Synthesis, characterization and cytotoxicity of glutathione- and PEG-glutathione-superparamagnetic iron oxide nanoparticles for nitric oxide delivery. Applied Surface Science, 367, 26–35.

Gupta, A.K. and Gupta, M. (2005) Synthesis and surface engineering of iron oxide nanoparticles for biomedical applications. Biomaterials, 26, 3995–4021.

Oka, C., Ushimaru, K., Horiishi, N., Tsuge, T. and Kitamoto, Y. (2015) Core–shell composite particles composed of biodegradable polymer particles and magnetic iron oxide nanoparticles for targeted drug delivery. Journal of Magnetism and Magnetic Materials, 381, 278–84.

Jeon, H., Kim, J., Lee, Y.M., Kim, J., Choi, H.W., Lee, J. et al. (2016) Poly-paclitaxel/cyclodextrin-SPION nano-assembly for magnetically guided drug delivery system. Journal of Controlled Release, 231, 68–76.

Kumar, R., Inbaraj, B.S. and Chen, B.H. (2010) Surface modification of superparamagnetic iron nanoparticles with calcium salt of poly(γ-glutamic acid) as coating material. Materials Research Bulletin, 45, 1603–7.

Kashyap, S., Pratihar, S.K. and Behera, S.K. (2016) Strong and ductile graphene oxide reinforced PVA nanocomposites. Journal of Alloys and Compounds, 684, 254–60.

Qiu, X.P. and Winnik, F. (2000) Preparation and Characterization of PVA Coated Magnetic Nanoparticles. Chinese Journal of Polymer, 18, 535–9.

Nadeem, M., Ahmad, M., Akhtar, M.S., Shaari, A., Riaz, S., Naseem, S. et al. (2016) Magnetic Properties of Polyvinyl Alcohol and Doxorubicine Loaded Iron Oxide Nanoparticles for Anticancer Drug Delivery Applications. PloS One, 11, e0158084.

Kim, S.Y., Ramaraj, B. and Yoon K, R. (2012) Preparation and Characterization of Polyvinyl alcohol-grafted Fe3O4 Magnetic Nanoparticles through Glutaraldehyde. Surface and Interface Analysis, 44, 91238– 1242.

Wahid, R. (2016) Sintesis dan Karakterisasi Nanopartikel Fe3O4 Dilapisi dengan Polivinil Alkohol dan Polivinil Alkohol- Glutaraldehid. Universitas Brawijaya.

Mahdavi, M., Ahmad, M., Haron, M., Namvar, F., Nadi, B., Rahman, M. et al. (2013) Synthesis, Surface Modification and Characterisation of Biocompatible Magnetic Iron Oxide Nanoparticles for Biomedical Applications. Molecules, 18, 7533–48.

Wu, W., He, Q. and Jiang, C. (2008) Magnetic Iron Oxide Nanoparticles: Synthesis and Surface Functionalization Strategies. Nanoscale Research Letters, 3, 397–415.

Petcharoen, K. and Sirivat, A. (2012) Synthesis and characterization of magnetite nanoparticles via the chemical co-precipitation method. Materials Science and Engineering: B, 177, 421–7.

Saxena, N. and Singh, M. (2017) Efficient synthesis of superparamagnetic magnetite nanoparticles under air for biomedical applications. Journal of Magnetism and Magnetic Materials, 429, 166–76.

Cornell, R.M. and Schwertmann, U. (2006) The Iron Oxides: Structure, Properties, Reactions, Occurrences and Uses. 2nd ed. Willey, Weinheim, Germany.

Unsoy, G., Yalcin, S., Khodadust, R., Gunduz, G. and Gunduz, U. (2012) Synthesis optimization and characterization of chitosan-coated iron oxide nanoparticles produced for biomedical applications. Journal of Nanoparticle Research, 14, 964.

Ikeya, M. (1993) New Applications of Electron Spin Resonance. Wspc, Osaka, Japan.

Teja, A.S. and Koh, P.-Y. (2009) Synthesis, properties, and applications of magnetic iron oxide nanoparticles. Progress in Crystal Growth and Characterization of Materials, 55, 22–45.

Niu, J.M. and Zheng, Z.G. (2014) Effect of Temperature on Fe3O4 Magnetic Nanoparticles Prepared by Coprecipitation Method. Advanced Materials Research, 900, 172–6.




DOI: http://dx.doi.org/10.21776/ub.natural-b.2018.004.03.1

Refbacks

  • There are currently no refbacks.